Functionalized Multiwalled Carbon Nanotube-Reinforced Polyimide Composite Films with Enhanced Mechanical and Thermal Properties

Polyimide- (PI-) based nanocomposites containing the 4,4-diaminodiphenyl ether- (ODA-) modified multiwalled carbon nanotube (MWCNT) filler were successfully prepared. The PI/MWCNTs-ODA composite films exhibit high thermal conductivity and excellent mechanical property. The optimal value of thermal conductivity of the PI/MWCNTs-ODA composite film is 0.4397?W/mK with 3?wt.% filler loading, increased by 221.89% in comparison with that of the pure PI film. In addition, the tensile strength of the PI/MWCNTs-ODA composite film is 141.48?MPa with 3?wt.% filler loading, increased by 20.74% in comparison with that of the pure PI film. This work develops a new strategy to achieve a good balance between the high thermal conductivity and excellent mechanical properties of polyimide composite films by using functionalized carbon nanotubes as an effective thermal conductive filler.

1. IntroductionPolyimide (PI) has been demonstrated one of the most important high-performance engineering plastics for its excellent mechanical property [13], thermal stability [4], and chemical resistance [5] because of its rigid-rod chemical structures, showing appealing potential in the area of electronic applications, membrane, insulating materials, and aerospace industry [610]. However, the very low thermal conductivity (0.1?W/mK) of PI can hardly meet the thermal requirements of electronic products, which limits its application in advanced microelectronics and aerospace applications. In order to facilitate the heat dissipation, it is necessary to further improve the thermal conductivity of PI. Therefore, improving the thermal conductivity of PI to endow it with better comprehensive performance has become a research focus. Introducing functional groups or elements into the main chain is an effective way to improve the performance of PI by lengthening the molecular chain and reducing the interaction between molecular chains. In addition, adding high thermal conductive fillers is another facile method to promote the thermal performance of PI [1117].

Various inorganic fillers owning high thermal conductivity have been added into the PI matrix by in situ polymerization to improve the overall performance of PI, including carbon black [18, 19], alumina (Al2O3) [20, 21], aluminum nitride (AlN) [22, 23], silica (SiO2) [24, 25], titanium dioxide (TiO2) [26], silicon carbide (SiC) [27, 28], silicon nitride (Si3N4) [29, 30], boron nitride (BN) [31, 32], and zinc oxide (ZnO) [33, 34]. Compared with the abovementioned inorganic fillers, carbon nanotubes (CNTs) possess high electrical conductivity (105?S·cm-1) and thermal conductivity (3500?W/mK) and extremely high Young modulus (0.9?TPa) and tensile strength (150?GPa), as well as excellent optical properties [35]. So, CNTs are considered to be the most optimal candidate as ideal enhancing fillers in high tensile, light weight polymer nanocomposites [3641]. Although CNTs have many merits, there are two major disadvantages that limit their reinforcing efficiency: (1) the bad dispersion of nanoparticles in the polymer matrix and (2) the weak interfacial interaction between nanoparticles and polymer matrix [4244].

Hence, increasing the dispersion of carbon nanotube nanoparticles in the polymer matrix and enhancing the interfacial interaction between nanoparticles and polymer matrix are critical troubles to make carbon nanotubes fully exert their potential to enhance the performance of the polymer matrix. Wang et al. [45] investigated graphene oxide@carbon nanotube- (GO/CNT-) reinforced PI; by the crosslinking between the amide bonds, the dispersibility of the nanoparticles in the polyimide matrix can be improved and the interfacial interaction between the nanoparticles and the PI matrix can be improved. Li et al. [46] reported that multiwalled carbon nanotubes (MWCNTs) were revised by polyacrylic acid, polyacrylamide, or poly(hydroxyethyl methylacrylate) which is used in the field of biomineralization. The polymer chains were deposited on the MWCNTs by photoinitiated polymerization of the monomers. Chen et al. [47] investigated the amine-treated MWCNTs/epoxy composites in which amine-treated MWCNTs were used as curing agents and are covalently grafted into the epoxy matrix. The tensile strength and impact strength of the composites increase with the content of MWCNTs, and the most significant improvement of the tensile strength is obtained with the addition of 1.5?wt.% amine-treated MWCNTs; the thermal stability of the nanocomposites also distinctly improves. In addition, different amine-treated graphenes, including ethylenediamine, diethylenetriamine, and p-phenylenediamine (EG, DG, and PG, respectively), were employed in synthesizing different contents of PI composites by in situ polymerization [48].

In this work, we prepared carboxylated carbon nanotubes; then, the carboxyl treated MWCNTs (MWCNTs-COOH) were reacted with 4,4-diaminodiphenyl ether (ODA) to obtain the amino carbon nanotubes (MWCNTs-ODA), which is used to synthesize PI composites by in situ polymerization. The PI composite films prepared by this method can improve the compatibility of CNTs with the PI matrix. The mechanical and thermal properties of PI/MWCNTs-ODA nanocomposite films were studied, while varying different contents in the MWCNTs-ODA.

2. Experimental2.1. MaterialsMultiwalled carbon nanotubes (MWCNTs) were obtained from Chengdu Organic Chemicals Co. Ltd., Chinese Academy of Sciences (China), with the length of 10-30 ?m; the outer diameter is 10-20?nm and a purity of >98%. Pyromellitic dianhydride (PMDA) (purity: >98.5%) and 4,4-diaminodiphenyl ether (ODA) (purity: >98.0%) were purchased from Sinopharm Chemical Reagent Co. Ltd., China. N,N-Dimethylacetamide (DMAc) (purity: >99.5%), N,N-dimethylformamide (DMF) (purity: >99.5%), and ethanol (purity: >99.7%) were purchased from Fuyu Fine Chemical Co. Ltd. (Tianjin, China). N,N-Dicyclohexylcarbodiimide (DCC) (purity: >99.0%) as a dehydrant and 4-dimethylaminopyridine (DMAP) (purity: >99.0%) as catalysts were purchased from Aladdin Industrial Corporation (Shanghai, China).

2.2. Synthesis of Amino-Functionalized MWCNTsIn a typical process of MWCNTs-COOH, 2?g pristine MWCNTs were mixed with 150?ml acid mixture of concentrated H2SO4 and concentrated HNO3 (volume ratio was 3?:?1). The mixture was treated with ultrasound for 1 hour at ambient temperature (KH-600 KDE, 600?W, 40?kHz) and dispersed evenly. The mixture was then poured into a 250?ml three-neck glass flask, followed by mechanical stirring under 70°C, oil bath for 24 hours. After that, the mixture was diluted with deionized water and precipitated and the supernatant was poured out, diluted, and precipitated multiple times. After centrifugation (TG-16, 8000?rpm, 10?min), we poured off the supernatant and then washed the remaining material with DMF until the pH is 7. Finally, the MWCNTs-COOH was obtained by overnight drying in a vacuum for 60°C.

Amino functional groups are grafted onto carboxylated carbon nanotube. In typical experiments, 0.2?g of MWCNTs-COOH, 20?ml of DMF, 2?g of ODA, 1?g of DCC, and 0.6?g of DMAP were mixed. Then, the mixed liquor was put into trinecked flask and magnetically stirred for 4 days at 100°C oil bath. After that, it was centrifuged (8000?rpm, 10?min) and washed with ethanol and the treated substance was put into a vacuum oven for 60°C (DZF-6020, 450?W, 50?Hz) to dry overnight to get MWCNTs-ODA. The specific synthesis process is shown in Scheme 1.

Scheme 1: The preparation process of MWCNTs-ODA.2.3. Preparation of WMCNTs-ODA/PI Nanocomposite FilmsThe preparation process of the PI/MWCNTs-ODA composite films includes the synthesis of PAA and preparation of PI. First, 2.2737?g (11.36?mmol) ODA was added in DMAc in a 100?ml trinecked flask, followed by stirring vigorously at room temperature for 30 minutes. Afterwards, 2.5263?g (11.58?mmol) PMDA (the molar ratio of PMDA and ODA was 1.02?:?1) was added in batches for six times, keeping the reaction temperature unchanged. After adding all PMDA, the mixture is kept in ice bath (temperature controlled at 2°C-10°C) for 1 hour. At the same time, 18.5?ml DMAc and a certain amount of prepared MWCNTs-ODA were mixed in the beaker, ultrasonic treatment for 1 hour at room temperature was done for even dispersion, and then MWCNTs-ODA/DMAc mixture was added to the reaction mixture in the ice bath. After the ice bath, the preparation of polyimide precursor polyamic acid (PAA)/MWCNTs-ODA mixture was casted on a clean glass substrate and the thickness was controlled within 1?mm, which was then put into the vacuum oven for 0.5?hour. The mixture underwent a series of thermal treatments afterwards; i.e., it was heated at 30°C for 1 hour, 50°C for 3 hours, 100°C for 1 hour, 200°C for 3 hours, and 250°C for 3 hours to complete the thermal imidization. WMCNTs-ODA/PI was prepared by natural cooling at room temperature. The solid content of the composite films was set at 8?wt.%, and the content of MWCNTs-ODA was set at 0?wt.%, 1?wt.%, 1.5?wt.%, 2?wt.%, 2.5?wt.%, 3?wt.%, and 4?wt.%, respectively. The specific synthesis process is shown in Scheme 2.

Scheme 2: The preparation process of MWCNTs-ODA/PI composite films.2.4. CharacterizationXRD (X-ray diffraction) patterns of the samples were analyzed by D8 ADVANCE (Bruker Ltd., Germany), employing Cu radiation (). The scanning was performed from 5°-85° at room temperature. FTIR (Fourier Transform infrared spectroscopy) of the samples was recorded by TENSOR II (Bruker Ltd., Germany), scanning from 500 to 4000?cm-1. TEM (transmission electron microscopy) of the samples was analyzed by JEOL JEM-2100 (Japan Electron Optics Laboratory Co. Ltd., Japan). Before the characterizations, the powder samples were dispersed in ethanol and ultrasound was performed for 30-60?minutes. TGA (thermal gravimetric analyses) were conducted on a DSC/TGA Discovery SDT 650 (TA, America) instrument from room temperature to 800°C with a heating rate of 10°C/min in the nitrogen environment. XPS (X-ray photoelectron spectroscopy) of the samples was recorded by ESCALAB 250XI (Thermo Fisher Scientific). Tensile samples were measured by CMT5105 (MTS Corporation, America). The stretching velocity is 500?mm/min, and the sample size is . SEM (scanning electron microscopy) of the samples was analyzed by Hitachi S-4800 (Hitachi, Japan). The thermal conductivity () of the sample () was measured by the TPS 2200 Hot Disk instrument (AB Corporation, Sweden). We place the sample between two parallel sensors (3.2?mm diameter), add 0.6?W power heat pulse with the duration of 20?s, and then record the corresponding thermal conductivity. The optical transmittance of composite films was examined by the UV-3600 spectrophotometer (Shimadzu Corporation, Japan); the wavelength range is 200-800?nm.

3. Results and Discussion3.1. Structure and Performance of MWCNTs, MWCNTs-COOH, and MWCNTs-ODAThe XRD patterns of pure MWCNTs, MWCNTs-COOH, and MWCNTs-ODA are shown in Figure 1(a); it can be seen that the XRD patterns of the pure carbon nanotubes and the modified carbon nanotubes are similar, indicating that the functionalized carbon nanotubes still have the same tubular structure compared with the original carbon nanotubes and the lattice spacing remains unchanged. The pure carbon nanotubes shows strong diffraction peaks at , 42°, and 77°. The functionalized carbon nanotubes have diffraction peaks at corresponding positions.

Figure 1: (a) XRD, (b) FTIR, and (c) TGA curves of MWCNTs, MWCNTs-COOH, and MWCNTs-ODA and TEM images of (d) MWCNTs, (e) MWCNTs-COOH, and (f) MWCNTs-ODA.The FTIR spectra of pure MWCNTs, MWCNTs-COOH, and MWCNTs-ODA are shown in Figure 1(b); the original carbon nanotubes have no obvious characteristic absorption peaks. In contrast, the MWCNTs-COOH exhibited stretching vibration absorption of C=O and C-O bonds at 1718?cm-1 and 1120?cm-1 and a characteristic peak of the O-H bond of the carboxyl group appeared at 3422?cm-1. It indicated that the carboxylic acid group was successfully grafted in the surface of the MWCNTs. Due to the formation of the amide bond, a stretching vibration peak of the C=O bond appeared at 1627?cm-1; the characteristic peak at 1318?cm-1 is due to the formation of the C-N bond in the amino functional group; the characteristic peak at 1495?cm-1 is formed by the C=C bond in the benzene ring; the characteristic peak at 1215?cm-1 is formed by the C-O bond in the aromatic ether; and the characteristic peak at 3443?cm-1 is due to the N-H bond in the amino functional group. These results suggested that the amino group in the ODA has been successfully grafted onto the CNTs.

The TEM images of pure MWCNTs, MWCNTs-COOH, and MWCNTs-ODA are shown in Figures 1(d)1(f); the pure CNTs show an obvious agglomeration, and the pipe wall is smooth, with a large aspect ratio and poor dispersion. After introducing the functional group, the aspect ratio of MWCNTs becomes smaller and the dispersion is more uniform, but the tube wall of the CNTs becomes rough. Compared with MWCNTs-COOH, the MWCNTs-ODA have a smaller aspect ratio, a rougher surface, and a significantly improved dispersibility.

The TGA of pure MWCNTs, modified MWCNTs-COOH, and modified MWCNTs-ODA are shown in Figure 1(c); thermogravimetric analysis of functionalized CNTs can provide more detailed information about the thermal stability and surface functionalization. The weight of pure CNTs at 800°C is 98.40%, because the CNTs themselves have excellent thermal stability and high temperature resistance, and the weight loss of 1.6% may be due to structural defects of the CNTs themselves. In contrast, carboxylated and aminated CNTs exhibit significant decomposition at lower temperatures. The carboxylated CNTs have a significant weight loss step at 220°C-290°C due to the degradation of carboxyl and hydroxyl groups in MWCNTs-COOH, and the carboxylated CNTs have a residual amount of 57.72% at 800°C. The aminated CNTs have a weight loss of approximately 34.13% in the range of 100°C-700°C; this is mainly due to the thermal decomposition of ODA grafted onto the CNTs. This further demonstrates that ODA is successfully grafted onto the surface of CNTs. In addition, we found that the aminated CNTs have a residual content of 64.07% at 800°C compared to carboxylated CNTs, with higher residuals due to the absence of hydroxyl groups in MWCNTs-ODA, and the benzene ring contained in ODA in MWCNTs-ODA has a stable structure. In other words, replacement of unstable hydroxyl groups in MWCNTs-COOH with more stable ODA groups, MWCNTs-ODA, possesses enhanced thermal stability.

X-ray photoelectron spectroscopy (XPS) analysis was performed to detect the group distribution of the MWCNTs and functionalized MWCNTs. The XPS of pure MWCNTs, modified MWCNTs-COOH, and modified MWCNTs-ODA is shown in Figure 2; the C 1s prominent peak of MWCNTs appeared at 284.8?eV in the test results [49, 50]. Compared with MWCNTs, the O 1s prominent peaks of MWCNTs-COOH and the N 1s prominent peaks of MWCNTs-ODA appeared at 532.6?eV and 399.5?eV, respectively, indicating the presence of O and N atoms in the sample. Among them, MWCNTs-COOH has significantly enhanced O 1s peak intensity compared with MWCNTs. MWCNTs-ODA has new N 1s peaks compared with MWCNTs and MWCNTs-COOH. This all indicates the successful modification of MWCNTs.

Figure 2: XPS spectrum of MWCNTs, MWCNTs-COOH, and MWCNTs-ODA.The dispersion of DMAc solvent, pure MWCNTs, MWCNTs-COOH, and MWCNTs-ODA is allowed standing for 0?h, 2?h, 4?h, and 8?h, respectively, as shown in Figure 3; we can find that the pure MWCNTs/DMAc mixture showed obvious deposition after standing for 2?h, while the MWCNTs-COOH/DMAc mixture and the MWCNTs-ODA/DMAc mixture dispersed well after standing for 2?h, and there was no obvious deposition appeared. After standing for 4?h and 8?h, the deposition of pure MWCNTs/DMAc mixture became more obvious. The MWCNTs-COOH/DMAc mixture showed deposition after standing for 8?h, while the MWCNTs-ODA/DMAc mixture maintained a very good dispersion. The reason is that after the functionalization of carbon nanotubes, the surface energy can be effectively reduced and the effect of aminated MWCNTs is better, so the dispersibility with organic solvents is better.

Figure 3: DMAc solvent, pure MWCNTs/DMAc mixture, MWCNTs-COOH/DMAc mixture, and MWCNTs-ODA/DMAc mixture allow standing for (a) 0?h, (b) 2?h, (c) 4?h, and (d) 8?h, respectively.3.2. Structural Characterization of the PI and MWCNTs-ODA/PI Composite FilmsIn order to study the structural characteristics of the pure PI and MWCNTs-ODA/PI composite films, XRD was performed; the result is shown in Figure 4(a). From previous tests, we can know the XRD pattern that the diffraction peak of carbon nanotubes at 2??=?26° is most obvious, while the diffraction peak of PI and MWCNTs-ODA is the same, indicating that the structures of PI chains and MWCNTs do not affect each other. In addition, MWCNTs-ODA has a large lattice spacing, so MWCNTs-ODA has good dispersibility and chemical compatibility in the PI matrix. From the XRD pattern, we found that the XRD of pure PI and MWCNTs-ODA/PI composite films is similar, mainly for two reasons. First, the monomers for synthesizing PI are ODA (diamine) and PMDA (dianhydride). The pure carbon nanotubes are also modified by ODA, so the pure PI and PI composite films contain the same monomer, which is not much different in the XRD pattern. Second, the MWCNTs-ODA content is very small and the performance in XRD is not obvious.

Figure 4: (a) XRD and (b) FTIR curves of pure PI and MWCNTs-ODA/PI composite films.The FTIR was used to detect the chemical bond of the composites [51, 52]. The FTIR spectra of pure PI and MWCNTs-ODA/PI composite films are shown in Figure 4(b); in the FTIR images of pure PI and PI composite films, the characteristic absorption peaks of imide groups appeared at 1778?cm-1 and 1707?cm-1, the characteristic peaks of C-N bonds appeared at 1363?cm-1, and the characteristic peaks of C=O bonds appeared at 722?cm-1. It indicated that PI imidization was fully completed. Due to the low content of MWCNTs-ODA in the PI matrix, many functional groups on the surface of MWCNTs-ODA could not be clearly observed in the FTIR results.

3.3. Thermal Properties of the PI and MWCNTs-ODA/PI Composite FilmsThermal stability is an important factor for the application of PI-based composites in high temperature environments [53, 54]. The thermal stability of the films was measured by a TG test under nitrogen atmosphere. The TGA of pure PI and MWCNTs-ODA/PI composite films are shown in Figure 5(a); compared with the work of Kalchounaki et al. [55], the composite film prepared by this work has better thermal stability. The weight loss of the pure PI film at 500°C was 2.1121%, and the residual at 800°C was 55.9794%. It can be seen that the weight loss of the pure PI film and PI/MWCNTs-ODA composite films at 500°C and 800°C is not much difference. There are two reasons for this phenomenon: first, only a small amount of aminated carbon nanotubes are added to the PI matrix, so there is no obvious difference in TGA curves; and second, although carbon nanotubes have significant weight loss between 100°C and 700°C after amino functionalization, due to good chemical compatibility and strong interaction between the aminated carbon tubes and the polyimide matrix, when the MWCNTs-ODA content is 3%, the weight loss at 500°C is 1.9077%, When the MWCNTs-ODA content is 3%, the weight loss at 500°C is 1.9077%. The corresponding data of thermal properties are summarized in Table 1.

Figure 5: (a) TGA and (b) thermal conductivity curves of pure PI and MWCNTs-ODA/PI composite films.Table 1: Thermal properties of pure PI and MWCNTs-ODA/PI composite films.The thermal conductivity curves of pure PI and MWCNTs-ODA/PI composite films are shown in Figure 5(b); compared with the work of Yan et al. [7], the composite film prepared by this work has better thermal conductivity. When the MWCNTs-ODA content increases from 0?wt.% to 4?wt.%, the thermal conductivity of the PI composite film increases with the increase of the MWCNTs-ODA content. Compared with pure PI (0.1366?W/mK), when the WMCNTs-ODA content is 3?wt.%, the thermal conductivity is 0.4397?W/mK. Its thermal conductivity is increased by 221.89%, because when the content of MWCNTs-ODA is low, the CNTs cannot form interconnected heat conduction channels and the carbon nanotubes appear in an isolated state in the PI matrix, which is like an “island-ocean” relationship, so the thermal conductivity is not obviously improved. When the content of carbon nanotubes is increased to 3?wt.%, the thermal conductivity is significantly improved, which is attributed to the fact that the MWCNTs-ODA nanofiller is connected to each other to form a heat conduction channel. The corresponding data of thermal conductivity are summarized in Table 2.

Table 2: Mechanical properties and thermal conductivity of pure PI and MWCNTs-ODA/PI composite films.3.4. Mechanical Properties of MWCNTs-ODA/PI Composite FilmsThe tensile strength of pure PI and MWCNTs-ODA/PI composite films is shown in Figure 6(a); compared with the work of Yan et al. [7], the composite film prepared by this work has better mechanical properties. It can be seen that the tensile strength of the pure PI film is 117.18?MPa. When the MWCNTs-ODA content increased from 0?wt.% to 3?wt.%, the tensile strength of the PI composite films significantly increased, and when the MWCNTs-ODA content was 3?wt.%, the tensile strength reached to 141.48?MPa, compared with pure PI increased by 20.74%. On the one hand, because the MWCNTs-ODA content is below 3?wt.%, the 3D network structure of MWCNTs cross-linking provides the intermolecular bonding force between PI and MWCNTs-ODA. When the composite film is subjected to external tensile force, the strong chemical bond between the MWCNTs-ODA and the PI chain can effectively transfer the stress of the PI chain to the surface of the MWCNTs-ODA and thus has excellent mechanical properties. Moreover, due to the good interaction and chemical compatibility between the aminated CNTs and PI matrix, the adhesion between them is obviously enhanced and the mechanical property is improved. However, when the MWCNTs-ODA content increased from 3?wt.% to 4?wt.%, the tensile strength of the PI composite film decreased significantly, because the additional amount of MWCNTs-ODA reaches the mechanical percolation threshold, and when the MWCNTs-ODA content is lower than this value, the MWCNTs-ODA nanofiller can be well dispersed in the PI matrix and the loading of the composite film can be increased to make the machine works. The performance is significantly improved, and when the MWCNTs-ODA content is higher than this value, the MWCNTs-ODA nanofiller is stacked in the PI matrix, which impairs the improvement of mechanical property. The corresponding data of mechanical properties are summarized in Table 2.

Figure 6: (a) Tensile strength curves of PI composite films and (b–h) SEM images of pure PI and MWCNTs-ODA/PI composite films with the MWCNTs-ODA content of 0?wt.%, 1?wt.%, 1.5?wt.%, 2?wt.%, 2.5?wt.%, 3?wt.%, and 4?wt.%, respectively.The fracture surface of the tensile test was observed by SEM, and the SEM images of pure PI and 1?wt.%, 1.5?wt.%, 2?wt.%, 2.5?wt.%, 3?wt.%, and 4?wt.% MWCNTs-ODA/PI composite films are shown in Figures 6(b)6(h), respectively; when the MWCNTs-ODA content is increased from 0?wt.% to 3?wt.%, it can be seen from the SEM image that the cross section of the MWCNTs-ODA/PI composite film has obvious break marks and the composite film is ductile fracture. At this time, the tensile strength of the MWCNTs-ODA/PI composite film increases with the increase of the MWCNTs-ODA content. In addition, when the content of MWCNTs-ODA is 3?wt.%, compared with pure PI, the cross section surface of the PI composite film is rough and there is obvious fracture surface in the enlarged view, due to the excellent interfacial adhesion and well compatibility between the PI matrix and the MWCNTs-ODA nanofiller; it is advantageous to transfer the tensile pressure from the polymer matrix to the MWCNTs-ODA nanofiller. When the MWCNTs-ODA content was increased from 3?wt.% to 4?wt.%, it can be seen from the SEM image that the cross section became significantly rougher and the MWCNTs-ODA/PI composite film was brittle fracture. Correspondingly, the tensile strength of the MWCNTs-ODA/PI composite film showed a significant decrease. Therefore, we conclude that the strong interaction between the nanofiller and the PI matrix makes the MWCNTs-ODA have good dispersibility and this is an important reason for the enhancement of mechanical properties of MWCNTs-ODA/PI nanocomposite films.

3.5. Optical Properties of MWCNTs-ODA/PI Composite FilmsThe optical properties of MWCNTs-ODA/PI composite films are shown in Figure 7; it shows the optical transmission of the MWCNTs-ODA/PI composite films with a thickness of 43-90 ?m in the range of 200-800?nm. The test was carried out with reference to a pure PI film. Due to the introduction of MWCNTs-ODA, the transmittance of composite films decreased from 92.172% (PI-1.5%) to 63.164% (PI-4%), and with the increase of the MWCNTs-ODA content, the color of the films became significantly deeper. The addition of MWCNTs-ODA has a significant effect on the optical properties of MWCNTs-ODA/PI composite films. When the content of MWCNTs-ODA is small, the difference in transmittance of the composite film is not obvious, because the MWCNTs-ODA content is extremely small, resulting in little change in light transmittance.

Figure 7: UV-vis spectral curves of PI composite films.4. ConclusionsIn summary, the XRD, FTIR, and XPS tests of MWCNT and MWCNTs-ODA demonstrated that the amino group was successfully grafted on CNTs without destroying the chemical structure of CNTs. The SEM, XRD, and FTIR tests of MWCNTs-ODA/PI composite films confirmed that the addition of MWCNTs-ODA did not destroy the structure and properties of the PI matrix and there was a strong interaction between MWCNTs-ODA and PI matrix and good chemical compatibility between MWCNTs-ODA and PI matrix. Through TGA data of pure PI and MWCNTs-ODA/PI composite films, we found that the addition of MWCNTs-ODA has little effect on the thermal stability of the PI matrix and the composite films has excellent thermal stability, which will not have significant weight loss before 500°C. Through the tensile test of the MWCNTs-ODA/PI composite film, we found that when the MWCNTs-ODA content is 3?wt.%, the tensile strength of the PI composite film is 141.48?MPa, which is 20.74% higher than that of the pure PI film. Through the thermal conductivity test of MWCNTs-ODA/PI composite films, we found that when the content of MWCNTs-ODA is 3?wt.%, the thermal conductivity of the PI composite film is 0.4397?W/mK, which is 221.89% higher than that of the pure PI film. Therefore, when the MWCNTs-ODA content is 3?wt.%, the MWCNTs-ODA/PI composite film has the best comprehensive performance, has excellent thermal conductivity and thermal stability, and might be further used as a potential heat dissipation material in the field of microelectronics and flexible circuit boards. In addition, we also found that as the MWCNTs-ODA content increases, the light transmittance is significantly reduced.

Data AvailabilityThe data used to support the findings of this study are included within the article.

DisclosureThe authors Min Chao and Yanming Li should be considered co-first authors.

Conflicts of InterestThe authors declare that there is no conflict of interest regarding the publication of this paper.

Authors’ ContributionsThe authors Min Chao and Yanming Li contributed equally to this work.

AcknowledgmentsThis work was financially supported by the Special Fund for Basic Scientific Research of Central Colleges, Chang’an University (Nos. 300102318403 and 300102319306), the National Science Foundation of China (No. 51407134), the China Postdoctoral Science Foundation (No. 2016M590619), the College Students Innovation and Entrepreneurship Training Program (No. 201810710121), the Natural Science Foundation of Shandong Province (No. ZR2019YQ24), and the Key Laboratory of Engineering Dielectrics and Its Application (Harbin University of Science and Technology), Ministry of Education. The authors also thank their colleagues in their laboratory for their support.

References
  • Q. Jiang, X. Wang, Y. Zhu, D. Hui, and Y. Qiu, “Mechanical, electrical and thermal properties of aligned carbon nanotube/polyimide composites,” Composites Part B: Engineering, vol. 56, pp. 408–412, 2014. View at Publisher · View at Google Scholar · View at Scopus
  • G. Wu, Y. Cheng, Z. Wang, K. Wang, and A. Feng, “In situ polymerization of modified graphene/polyimide composite with improved mechanical and thermal properties,” Journal of Materials Science: Materials in Electronics, vol. 28, no. 1, pp. 576–581, 2017. View at Publisher · View at Google Scholar · View at Scopus
  • M. Cai, J. Zhu, C. Yang, R. Gao, C. Shi, and J. Zhao, “A parallel bicomponent TPU/PI membrane with mechanical strength enhanced isotropic interfaces used as polymer electrolyte for lithium-ion battery,” Polymers, vol. 11, no. 1, p. 185, 2019. View at Publisher · View at Google Scholar
  • M. Chao, “Synthesis and characterization of semicrystalline polyimides containing bridged linkages,” International Journal of Polymer Science, vol. 2018, Article ID 8590567, 7 pages, 2018. View at Publisher · View at Google Scholar · View at Scopus
  • Z. Ahmad and J. E. Mark, “Polyimide-ceramic hybrid composites by the sol-gel route,” Chemistry of Materials, vol. 13, no. 10, pp. 3320–3330, 2001. View at Publisher · View at Google Scholar · View at Scopus
  • S. Jiang, H. Hou, S. Agarwal, and A. Greiner, “Polyimide nanofibers by “green” electrospinning via aqueous solution for filtration applications,” ACS Sustainable Chemistry & Engineering, vol. 4, no. 9, pp. 4797–4804, 2016. View at Publisher · View at Google Scholar · View at Scopus
  • W. Yan, Y. Zhang, H. Sun et al., “Polyimide nanocomposites with boron nitride-coated multi-walled carbon nanotubes for enhanced thermal conductivity and electrical insulation,” Journal of Materials Chemistry A, vol. 2, no. 48, pp. 20958–20965, 2014. View at Publisher · View at Google Scholar · View at Scopus
  • J. Dong, C. Yin, X. Zhao, Y. Li, and Q. Zhang, “High strength polyimide fibers with functionalized graphene,” Polymer, vol. 54, no. 23, pp. 6415–6424, 2013. View at Publisher · View at Google Scholar · View at Scopus
  • X. Xue, H. Yan, and Y. Fu, “Preparation of pure and metal-doped Li4Ti5O12 composites and their lithium-storage performances for lithium-ion batteries,” Solid State Ionics, vol. 335, pp. 1–6, 2019. View at Publisher · View at Google Scholar · View at Scopus
  • Z. Li, K. Kou, J. Xue, C. Pan, and G. Wu, “Study of triazine-based-polyimides composites working as gel polymer electrolytes in ITO-glass based capacitor devices,” Journal of Materials Science: Materials in Electronics, vol. 30, no. 4, pp. 3426–3431, 2019. View at Publisher · View at Google Scholar · View at Scopus
  • W. Dai, J. Yu, Z. Liu et al., “Enhanced thermal conductivity and retained electrical insulation for polyimide composites with SiC nanowires grown on graphene hybrid fillers,” Composites Part A: Applied Science and Manufacturing, vol. 76, pp. 73–81, 2015. View at Publisher · View at Google Scholar · View at Scopus
  • L. Zuo, W. Fan, Y. Zhang et al., “Graphene/montmorillonite hybrid synergistically reinforced polyimide composite aerogels with enhanced flame-retardant performance,” Composites Science and Technology, vol. 139, pp. 57–63, 2017. View at Publisher · View at Google Scholar · View at Scopus
  • Y. Qin, Q. Peng, Y. Ding et al., “Lightweight, superelastic, and mechanically flexible graphene/polyimide nanocomposite foam for strain sensor application,” ACS Nano, vol. 9, no. 9, pp. 8933–8941, 2015. View at Publisher · View at Google Scholar · View at Scopus
  • T. Zhang, Y. Zhao, and K. Wang, “Polyimide aerogels cross-linked with aminated Ag nanowires: mechanically strong and tough,” Polymers, vol. 9, no. 12, p. 530, 2017. View at Publisher · View at Google Scholar · View at Scopus
  • Y. Song, H. Yao, H. Tan et al., “Synthesis and memory characteristics of highly organo-soluble hyperbranched polyimides with various electron acceptors,” Journal of Polymer Science Part A: Polymer Chemistry, vol. 55, no. 14, pp. 2281–2288, 2017. View at Publisher · View at Google Scholar · View at Scopus
  • X. Li, J. Wang, Y. Zhao, and X. Zhang, “Template-free self-assembly of fluorine-free hydrophobic polyimide aerogels with lotus or petal effect,” ACS Applied Materials & Interfaces, vol. 10, no. 19, pp. 16901–16910, 2018. View at Publisher · View at Google Scholar · View at Scopus
  • X. Lei, M. Qiao, L. Tian, Y. Chen, and Q. Zhang, “Tunable permittivity in high-performance hyperbranched polyimide films by adjusting backbone rigidity,” The Journal of Physical Chemistry C, vol. 120, no. 5, pp. 2548–2561, 2016. View at Publisher · View at Google Scholar · View at Scopus
  • S. Han, J. T. Lin, Y. Yamada, and D. D. L. Chung, “Enhancing the thermal conductivity and compressive modulus of carbon fiber polymer–matrix composites in the through-thickness direction by nanostructuring the interlaminar interface with carbon black,” Carbon, vol. 46, no. 7, pp. 1060–1071, 2008. View at Publisher · View at Google Scholar · View at Scopus
  • C. K. Leong, Y. Aoyagi, and D. D. L. Chung, “Carbon black pastes as coatings for improving thermal gap-filling materials,” Carbon, vol. 44, no. 3, pp. 435–440, 2006. View at Publisher · View at Google Scholar · View at Scopus
  • X. Liang, Y. Yang, X. Jin, Z. Huang, and F. Kang, “The high performances of SiO2/Al2O3-coated electrospun polyimide fibrous separator for lithium-ion battery,” Journal of Membrane Science, vol. 493, pp. 1–7, 2015. View at Publisher · View at Google Scholar · View at Scopus
  • H. Wang, H. Li, L. Yu, Y. Jiang, and K. Wang, “Synthesis of porous Al2O3-PVDF composite separators and their application in lithium-ion batteries,” Journal of Applied Polymer Science, vol. 130, no. 4, pp. 2886–2890, 2013. View at Publisher · View at Google Scholar · View at Scopus
  • Y. Zhou, H. Wang, L. Wang et al., “Fabrication and characterization of aluminum nitride polymer matrix composites with high thermal conductivity and low dielectric constant for electronic packaging,” Materials Science and Engineering: B, vol. 177, no. 11, pp. 892–896, 2012. View at Publisher · View at Google Scholar · View at Scopus
  • B. L. Zhu, J. Wang, J. Ma, J. Wu, K. C. Yung, and C. S. Xie, “Preparation and properties of aluminum nitride-filled epoxy composites: effect of filler characteristics and composite processing conditions,” Journal of Applied Polymer Science, vol. 127, no. 5, pp. 3456–3466, 2013. View at Publisher · View at Google Scholar · View at Scopus
  • Y. Zhou, L. Wang, H. Zhang, Y. Bai, Y. Niu, and H. Wang, “Enhanced high thermal conductivity and low permittivity of polyimide based composites by core-shell Ag@SiO2 nanoparticle fillers,” Applied Physics Letters, vol. 101, no. 1, article 012903, 2012. View at Publisher · View at Google Scholar · View at Scopus
  • M. Shanthil, R. Thomas, R. S. Swathi, and K. George Thomas, “Ag@SiO2 core–shell nanostructures: distance-dependent plasmon coupling and SERS investigation,” The Journal of Physical Chemistry Letters, vol. 3, no. 11, pp. 1459–1464, 2012. View at Publisher · View at Google Scholar · View at Scopus
  • G. Wu, J. Li, K. Wang, Y. Wang, C. Pan, and A. Feng, “In situ synthesis and preparation of TiO2/polyimide composite containing phenolphthalein functional group,” Journal of Materials Science: Materials in Electronics, vol. 28, no. 9, pp. 6544–6551, 2017. View at Publisher · View at Google Scholar · View at Scopus
  • Z. Yuan, J. Yu, B. Rao et al., “Enhanced thermal properties of epoxy composites by using hyperbranched aromatic polyamide grafted silicon carbide whiskers,” Macromolecular Research, vol. 22, no. 4, pp. 405–411, 2014. View at Publisher · View at Google Scholar · View at Scopus
  • Y. Niu, X. Zhang, J. Zhao, Y. Tian, Y. Li, and X. Yan, “Preparation, characterization and properties of amine-functionalized silicon carbide/polyimide composite films,” RSC Advances, vol. 4, no. 54, article 28456, 2014. View at Publisher · View at Google Scholar · View at Scopus
  • W. Zhou, C. Wang, T. Ai, K. Wu, F. Zhao, and H. Gu, “A novel fiber-reinforced polyethylene composite with added silicon nitride particles for enhanced thermal conductivity,” Composites Part A: Applied Science and Manufacturing, vol. 40, no. 6-7, pp. 830–836, 2009. View at Publisher · View at Google Scholar · View at Scopus
  • Y. Zhou, H. Hyuga, D. Kusano, Y. Yoshizawa, and K. Hirao, “A tough silicon nitride ceramic with high thermal conductivity,” Advanced Materials, vol. 23, no. 39, pp. 4563–4567, 2011. View at Publisher · View at Google Scholar · View at Scopus
  • J. Hou, G. Li, N. Yang et al., “Preparation and characterization of surface modified boron nitride epoxy composites with enhanced thermal conductivity,” RSC Advances, vol. 4, no. 83, pp. 44282–44290, 2014. View at Publisher · View at Google Scholar · View at Scopus
  • K. Sato, H. Horibe, T. Shirai et al., “Thermally conductive composite films of hexagonal boron nitride and polyimide with affinity-enhanced interfaces,” Journal of Materials Chemistry, vol. 20, no. 14, p. 2749, 2010. View at Publisher · View at Google Scholar · View at Scopus
  • S. Uchida, T. Murakami, T. Iwamura, R. Ishige, and S. Ando, “Enhanced thermal conductivity in immiscible polyimide blend composites with needle-shaped ZnO particles,” RSC Advances, vol. 7, no. 25, pp. 15492–15499, 2017. View at Publisher · View at Google Scholar · View at Scopus
  • D. Yorifuji and S. Ando, “Enhanced thermal conductivity over percolation threshold in polyimide blend films containing ZnO nano-pyramidal particles: advantage of vertical double percolation structure,” Journal of Materials Chemistry, vol. 21, no. 12, p. 4402, 2011. View at Publisher · View at Google Scholar · View at Scopus
  • P. Kim, L. Shi, A. Majumdar, and P. L. McEuen, “Thermal transport measurements of individual multiwalled nanotubes,” Physical Review Letters, vol. 87, no. 21, article 215502, 2001. View at Publisher · View at Google Scholar · View at Scopus
  • R. H. Baughman, C. Cui, A. A. Zakhidov et al., “Carbon nanotube actuators,” Science, vol. 284, no. 5418, pp. 1340–1344, 1999. View at Publisher · View at Google Scholar · View at Scopus
  • M. J. Esplandiu, V. G. Bittner, K. P. Giapis, and C. P. Collier, “Nanoelectrode scanning probes from fluorocarbon-coated single-walled carbon nanotubes,” Nano Letters, vol. 4, no. 10, pp. 1873–1879, 2004. View at Publisher · View at Google Scholar · View at Scopus
  • M. Cadek, J. N. Coleman, K. P. Ryan et al., “Reinforcement of polymers with carbon nanotubes: the role of nanotube surface area,” Nano Letters, vol. 4, no. 2, pp. 353–356, 2004. View at Publisher · View at Google Scholar · View at Scopus
  • C. Wei, D. Srivastava, and K. Cho, “Thermal expansion and diffusion coefficients of carbon nanotube-polymer composites,” Nano Letters, vol. 2, no. 6, pp. 647–650, 2002. View at Publisher · View at Google Scholar · View at Scopus
  • K. Wang, Y. H. Chang, C. Zhang, and B. Wang, “Conductive-on-demand: tailorable polyimide/carbon nanotube nanocomposite thin film by dual-material aerosol jet printing,” Carbon, vol. 98, pp. 397–403, 2016. View at Publisher · View at Google Scholar · View at Scopus
  • L. Yan, G. Zhang, L. Zhang et al., “Robust construction of underwater superoleophobic CNTs/nanoparticles multifunctional hybrid membranes via interception effect for oily wastewater purification,” Journal of Membrane Science, vol. 569, pp. 32–40, 2019. View at Publisher · View at Google Scholar ·
  • Publication date: 14/08/2019

    Author: Min Chao,1 Yanming Li,1 Guanglei Wu,2,3 Zhenjun Zhou,1 and Luke Yan1

    Reference: International Journal of Polymer ScienceVolume 2019, Article ID 9302803, 12 pageshttps://doi.org/10.1155/2019/9302803

    International Journal of Polymer Science



          

    This project has received funding from the Bio Based Industries Joint Undertaking under the European Union’s Horizon 2020 research and innovation programme under grant agreement No 837761.